Magnetically enhanced coaxial cable with improved time delay characteristics

ABSTRACT

A magnetically enhanced coaxial cable of the type having a center conductor, a dielectric spacer around the center conductor and a conductive shield around the dielectric spacer, said magnetic enhancement comprising a thin layer of circumferentially oriented uniaxial anisotrophic magnetic material having high conductivity and high permeability adapted to transmit wave energy and conventional current without being switched or reoriented. The magnetic enhancement provides an increase inductance and current carrying capacity without corresponding increases in time delay and other losses associated with magnetic loading.

United States Patent [191 Lorber et al.

[451 May 27, 1975 1 MAGNETICALLY ENHANCED COAXIAL CABLE WITH IMPROVED TIME DELAY CHARACTERISTICS [75] Inventors: Harold Lorber, Dresher; Irving Duboff, West Chester, both of Pa.

[73) Assignee: Hilabs Company, Wilmington, Del.

[22] Filed: Mar. 5, 1973 [21] Appl. No.: 338,335

[52] U.S. Cl. 333/96; 178/45; 333/31 [51] Int. Cl ..HOIp 3/06;H0lb 11/14 [58] Field of Search 178/45; 333/96, 31 R, 24.2,

[561 References Cited UNITED STATES PATENTS 2,387,783 10/1945 Tawney 178/45 3,175,200 3/1965 Hoffman et a1. 340/174 TL 3,320,554 5/1967 Wieder 333/241 3,399,361 8/1968 333/31 R 3,460,114 8/1969 Chow 340/174 TL 3,479,619 11/1969 Tuan-ngo 333/31 R FOREIGN PATENTS OR APPLICATIONS 296,114 8/1928 United Kingdom 174/45 529,931 12/1940 United Kingdom 178/45 OTHER PUBLICATIONS Kehler & Coren; J. Appl. Phys. 41 pp. 1346-1347, March 1970.

Thomas, H. Magnetically Controllable Delay Line," IBM Tech. Disclosure Bulletin, Vol. 8, No. 11, 4-1966, pp. 1592-1593.

English et al., Integrated Transmission Lines for Magnetic Thin Film Memories, IEEE. Trans. on Magnetics, Vol. MAG-l, 12-1965, pp. 272-276. Ferguson, E. T., Uniaxial Magnetic Anisotropy Induced in Fe-Ni Alloys by Magnetic Anneal," Jr. of Applied Physics, 29, 3-1958, pp. 252-253.

Hoffman et 211., High Speed Digital Storage Using Cylindrical Magnetic Films, Jr. of British IRE, 1-1960, pp. 31-36.

Primary Examiner-Alfred E. Smith Assistant Examiner-Wm. H. Punter [57] ABSTRACT A magnetically enhanced coaxial cable of the type having a center conductor, a dielectric spacer around the center conductor and a conductive shield around the dielectric spacer, said magnetic enhancement comprising a thin layer of circumferentially oriented uniaxial anisotrophic magnetic material having high conductivity and high permeability adapted to trans mit wave energy and conventional current without being switched or reoriented. The magnetic enhancement provides an increase inductance and current carrying capacity without corresponding increases in time delay and other losses associated with magnetic loading.

16 Claims, 6 Drawing Figures MAGNETICALLY ENHANCED COAXIAL CABLE WITH IMPROVED TIME DELAY CHARACTERISTICS BACKGROUND OF THE INVENTION This invention relates to coaxial transmission cables for use in transmission of both conventional current and electromagnetic waves. More particularly, this invention relates to a magnetically loaded transmission cable which has greater current carrying capabilities that previously known cables of equal size or alternatively the novel magnetically loaded transmission cable is capable of being made smaller in size and volume than previously known cables without causing increases in losses or time delay normally accompanying magnetic loading.

Heretofore, it was known that magnetically loading a coaxial transmission cable would increase the inductance of the line. As the inductance increases, characteristic impedance and the time delay increases in conventional coaxial cables. Heretofore, it was desirable to increase the inductance by magnetic loading to de crease attenuation even though magnetic loading introduces hysteresis and eddy current losses and causes time delays.

Magnetic loading materials spaced in the dielectric of coaxial cables are described in US. Pat. Nos. 2,787,656; 2,929,034 and 2,727,945. These and other magnetic loading teaching are generally concerned with high resistance and high permeability ferrities which by their structural nature are large or relatively thick and are not applicable for use in microminiature cables. Thin film magnetically coated conductors have been employed in plated wire memory planes such as those shown in U.S. Pat. No. 3,460,] 14, however, such rigid planes are generally concerned with reducing the characteristic impedance of an unshielded insulated memory wire. Plated memory wires are not uniformly shielded and are designed to switch from one state to another by coupling magnetic fields.

There has long been a need to reduce the size and weight of flexible coaxial cables. Our co-pending application Ser. No. 266,345 filed June 26, I972 for Improved Coaxial Cable" solves many of these problems. These and prior art structures were accompanied by increases in time delay. Coaxial cable for high speed computers and communications equipment require minimized time delays as well as miniaturization. Major computer manufacturers and coaxial cable manufacturers have recognized this need but have not miniaturized conventional coaxial cables by magnetic loading. Since computer advances are often accomplished through faster operations embodied in solid state devices, the need for faster propagation of electrical pulse energy has become almost as important as miniaturization of the circuitry.

BRIEF SUMMARY OF THE INVENTION The present invention provides a coaxial cable having increased characteristic impedance achieved through magnetic loading which increases the inductive reactance and decreases the attenuation, however, the increase in inductive reactance is not accompanied by the usual expected increase in time delay. The means employed to achieve magnetic loading do not increase the eddy current and hysteresis losses or other losses which would detract from the use of the novel coaxial cable as a miniaturized high frequency coaxial transmission cable.

A principle object of this invention is to reduce the size and weight of a coaxial cable without changing its characteristic impedance or increasing losses and time delay.

Another object of the present invention is to minimize time delay of coaxial cables while increasing the inductive reactance.

Another object of the present invention is to provide a method for producing a series of microminiature c0- axial cables having new and desirable attenuation and time delay characteristics.

Another object of the present invention is to provide means for conducting larger amounts of conventional current without increasing the overall size of a coaxial cable.

Accordingly, there is provided a conventional coaxial cable structure comprising a center conductor and an outer shield separated by a dielectric spacer. The center conductor is further provided with a thin film of circumferentially oriented uniaxial anisotropic magnetic material having a thickness much less than the diameter of the center conductor but thicker than the skin depth thickness at the desired highest frequency of the operation. Means supplying electrical energy to the center conductor are preferably limited to an operational level or direction which prevents switching of magnetic orientation, thus permitting the minimum delay time in wave propagation. These and other features of the present invention will be set forth in greater detail in the following description.

DESCRIPTION OF THE DRAWINGS FIG. 1 is a transverse sectional view ofa miniaturized coaxial cable constructed in accordance with teachings of this invention;

FIG. 2 is a longitudinal section view ofa miniaturized coaxial cable constructed in accordance with the teachings of this invention;

FIG. 3 is a simplified equivalent network circuit of a conventional coaxial cable;

FIG. 4 is a typical B vs. H curve for square loop high permeability magnetic material;

FIG. 5 is a schematic curve showing current density vs. distance from the center of a center conductor;

FIG. 6 is a simplified equivalent network circuit of the new coaxial cable.

DESCRIPTION OF THE PREFERRED EMBODIMENT FIGS. 1 and 2 show a coaxial cable 10 constructed in accordance with a preferred embodiment of this invention. The cable comprises a center conductor 11 of conductive material such as copper, copper-beryllium or other high strength conductive alloys. A thin conductive coating of magnetic material 12 is conductively attached to the center conductor 11 directly or to an extremely thin base conductive layer (not shown) on the center conductor 11.

The thin layer of magnetic material 12 is preferably circumferentially oriented with an easy magnetization axis transverse to the direction of wave propagation. Conversely, the hard magnetization axis is axially aligned with the direction of wave propagation to assure the preferred mode of operation of the invention. It has been found that uniaxial anisotropic Ni-Fe films 500A to approximately 15,000A thick provide a desirable oriented film for the preferred embodiments hereinafter explained.

A preferred method of providing the desired uniaxial anisotropic orientation is to plate the desired magnetic layer 12 onto the center conductor H in the presence of a strong circumferentially oriented magnetic field such as that which occurs when a strong d.c. conduction current is passed through the center conductor 11. The center conductor 11 may be annealed and then placed in the presence of strong circumferential field while the magnetic layer 12 is cooled from above its recrystallization temperature. Reheating and reorienting may be necessary when stress relieving a plated center conductor ll or when hot processes are employed to attach the dielectric spacer 14.

A dielectric spacer l4 surrounds the magnetically coated center conductor 11 and a continuous conductive shield 13 surrounds the dielectric spacer 14. The shield 13 may be protected by an insulating layer or jacket 16.

It was discovered that the novel coaxial transmission cable did not operate in a manner to be expected by the addition of a magnetic loading material. The operating characteristics of the coaxial cable shown in FIGS. 1 and 2, both with and without magnetic loading materials may be defined by equivalent circuit formulas. A simplified equivalent network circuit for a conventional coaxial cable is shown in FIG. 3.

The series inductance L of an equivalent tee section coaxial transmission cable has been defined by the characteristic impedance Z by the attenuation a by alt;

log

where p. is the permeability of the dielectric, e is the dielectric constant of the dielectric spacer, D is the inside diameter of the outer shield, d is the outside diameter of the center conductor, R is the series resistance, C is the shunt capacitance and G is the shunt conductance.

The values in a standard original coaxial cable may be designated by subnotation and values of prior art magnetically loaded coaxial cable may be designated by sub-r notations. Adding a very thin layer of magnetic material to the center conductor will increase the inductance L to L, without measurably changing the spacing of the elements, the dielectric constant e of the dielectric spacer 14 or the shunt capacitance C.

Formula (l) indicates that the inductance L, increases with an increase in resultant permeability p.,. Formula (2) indicates that the shunt capacity C is inversely proportional to D/d and directly proportional to the dielectric constant 6. Formula (3) indicates that characteristic impedance Z, increases with an increase in inductance L,. Formula (4) indicates that attenuation or, decreases with an increase in inductance L, as the first term of formula (4) is large compared to the second term. Formula (5) indicates that time delay T, increases with an increase in inductance L, and effective permeability ,|.r.,v

A piece of standard construction coaxial cable hav ing an impedance of 17 ohms was found to have a time delay T of approximately 1.5 nanoseconds per foot. An increase of the resultant t, over 11., by a factor of five would ordinarily increase both Z, and T, by the square root of five. Applicants have been able to so increase Z, without a corresponding increase in T,.

In one series of tests the time delay of a seventeen ohm coaxial cable appeared to be unchanged or reduced even though the inductance L, and characteristic impedance Z, were increased. A piece of the novel coaxial cable was altered to change the circumferentially oriented easy axis of the uniaxial anisotropic layer of thin magnetic material 12 to a partially isotropic layer. The time delay T, of the altered sample almost doubled. For comparison purposes, it has been established by test and calculations that a seventeen ohm coaxial cable can be increased to 50 ohms by magnetically loading the cable. Ordinarily magnetic loading would increase the time delay from 1.5 nanoseconds per foot, to over 4.0 nanoseconds per foot. The time delay of the magnetically enhanced cable constructed according to the present invention remained at approx imately 1.5 nanoseconds per foot, however, when the same coated center conductor was partially annealed to partially destroy the desired magnetic orientation the time delay increased to over 2.5 nanoseconds per foot.

It was discovered that Ni 20% Fe Permalloy plated on copper beryllium center conductors to a thickness of 8,000A to 10,000A in a manner which provides a circumferentially oriented magnetic easy axis, when made into the novel coaxial cable, increased the characteristic impedance Z, without an appreciable increase in time delay T, over T Initial results indicate that the time delay may be as low as or below that obtained for coaxial cables without magnetic loading.

The properties of uniaxial anisotropic material may be enhanced by first coating a flash layer of copper on the center conductor. It is believed that the copper or other conductive undercoat aids in maintaining uniform anisotropy and masks structural defects in the center conductor. Thin films 500A to about 15,000A thick have been made which have easy axis and hard axis orientation. It may be desirable, as in plated wire memories, to restrict the magnetostriction effects to a minimum as usually occurs in Permalloy films having approximately 80% nickel. Films which have the above described circumferential easy axis orientation may be made by plating, vacuum deposition and sputtering in the presence of a circumferentially oriented magnetic field. Other film techniques such as cladding, rolling, evaporation, drawing, chemical deposition and suspen sion deposition may require post operative annealing in an induced magnetic field.

Nickel iron alloys and other conductive magnetic materials which have crystalline grain structure may be coated on the center conductor and then cold drawn so as to create a preferred desired oriented magnetic field.

The plated thin films were deposited or treated in a magnetic field so that the preferred orientation was circumferential and the film displayed high anisotropy. The clad and drawn nickel iron wires, known to have a crystalline grain structure, were oriented mechanically through the process of drawing. Annealing the drawn wire does not have to destroy the high anisotropy developed mechanically, thus, drawn wire may be more stable for commercial purposes. Solid magnetic drawn wires display the desirable permeability increase but are not as conductive as clad wires. While the special crystal orientation is not well understood, it is presumed that an apparent effective internal magnetic field is present as a result of interaction of grain crystals and the high effective internal field. This magnetic field is present at the wall of the center conductor which forms the wave guide. There appears to be a faster phase change as a result of the oriented magnetic field and the time delay is decreased (increase in phase velocity).

Another feature of the present invention requires that the thin layer of magnetic material 12 be relatively conductive so that the radial electrical field E at the boundry of the center conductor be continuous, as will be explained. Permalloy type thin films are considered to be high permeability, low resistance films, whereas ceramic ferrites are considered to be high resistance, high permeability materials which do not conduct conventional current.

The dielectric material 14 can be any low loss dielectric preferably having a dielectric constant in the range of e 1.2 to 3.5. The dielectric constant for air is 1.0 and for foamed plastics may be as low as 1.3, however, Teflon which is desirable for many uses is 2.1. Materials known to be used in coaxial cables such as Mylar, polyethylene, polypropylene and other polyolefins are also useful in the present novel cable. The shield 13 is made from a conductor which has low loss at operating frequencies. Copper braid is sometimes employed because it is known to act as a closed shield below 1000 megahertz. Solid copper in the form of film, wire, foil or foil supported on insulating tapes may be employed. It is desirable that the shield 13 be conductive and at least twice the skin depth thickness at the upper frequency of operation as is the case for coaxial cable outer shields.

The outer insulation layer 16 may be any typical electrical insulation and may be applied as a tape either with or without the shield 13.

High permeability materials usually have high eddy current and hysteresis losses. Ferrites have been employed as magnetic loading materials in coaxial cables because the B vs H loop is narrow indicating that low hysteresis losses are to be expected. FIG. 4 illustrates an open B vs H loop of the type obtained with thin films or Permalloy materials, where B is the flux density and H is the magnetizing force intensity. The permeability u of a material is defined as u B/H. The slope of the curve is substantially horizontal in the saturation region, and substantially vertical in the unsaturated region. It can be seen that the incremental permeability p A will increase if the magnetizing force H switches the saturation region from negative to positive saturation. The incremental permeability u A of uniaxial anisotropic films may be held substantially constant at very small values (about 5 gauss per oersted, thus it is possible to transmit pulse power in the novel coaxial transmission cable by remaining on a horizontal portion p. A of the B vs H curve, such as operating between point 21 and 22 on the curve without incurring time delay increases as would be incurred if operating at maximum permeability.

it has been found that ohm novel transmission cable may be operated in a conventional mode with very high frequency pulse power surges up to three fourths of a watt without switching the magnetic orientation or incurring hysteresis or eddy current losses. The novel coaxial cables may be used within the usual power ranges for standard coaxial cables without encountering undesirable effects.

lf the aforementioned formulas (l), (2) and (3) are combined it can be shown that Z v L/C and As is well known, when the value of D/d approaches 3.59, attenuation a approaches a minimum and Z at minimum attenuation is approximately 77 ohms. Heretofore, it has been the practice to make some small coaxial cable having 50, 75, and ohm impedances and having center conductors of 0.008, 0.010 and 0.010 inches diameter respectively. Such coaxial cables employing a Teflon dielectric require D/d ratios of 2.3, 3.4 and 5.3 respectively when no magnetic loading is employed. Prior attempts to decrease the cable size without magnetic loading, increased the characteristic impedance and attenuation. Prior attempts to decrease attenuation were directed to an increase in inductance L and characteristic impedance Z through magnetic loading without a decrease in cable size.

Employing the present invention and maintaining the same center conductor as employed in the above mentioned prior art 50, 75 and 100 ohm coaxial cables, the D/d ratio of the new novel 50, 75 and 100 ohm coaxial cables may be reduced as follows: for 50 ohm cable D/d of 2.3 is reduced to 1.4, for 75 ohm cable D/d of 3.5 is reduced to 2.2 and for 100 ohm cable, D/d of 5.3 is reduced to 3.0. These figures are rounded representing a resultant or effective permeability p, of 5 and a dielectric constant 68 for Teflon of 2.1.

It will be understood that the values of u, and 6 may be changed and the desired impedance values of 50, 75 and 100 ohms maintained. As the D/d ratio is reduced and approaches unity the maximum values of u, required to achieve the desired impedance are obtained as follows. If e is 1.0 as in air, t, approaches 53 for 50 ohm cable; 12.2 for 75 ohm cable and 28 for 100 ohm cable. If 68 is 1.6 as with foamed plastic, t, approaches 8.3 for 50 ohm cable; 23.4 for 75 ohm cable and 68.8 for 100 ohm cable. 1f e is 2.1 as with Teflon 11., approaches 11.2 for 50 ohm cable; 37.6 for 75 ohm cable and 126 for 100 ohm cable. Permalloy thin films which are oriented by a magnetic field or by cold drawing of the type employed are capable of achieving values of t, below the above five (the value employed for a preferred embodiment). Other magnetic thin film materials having the range of permeabilities described and having the above-mentioned desire uniaxial circumferential orientation may be employed.

Reduction of the ratio of D/d while maintaining the impedance Z constant permits microminiature coaxial cable to be designed. The inside diameter D of the shield can now be reduced without increasing time delay or other losses which normally accompanied magnetic loading impedance increases. Had the novel coaxial cable been available heretofore it could have been employed in aircraft and spacecraft electronics systems to decrease weight of the coaxial cables by up to 50 percent and further decrease the size and weight of the electronic hardware.

It is known that conventional current is displaced to the outside annular area of a conductor as frequency increases. FIG. 5 shows schematically how the current density increases exponentially toward the outer diameter of the center conductor 11. At the center 23, where the radius r=0, the current density is substantially zero at high frequency and rises to a maximum at the outer diameter 24 of the center conductor. Due to skin effect phenomenon the current density is believed to fall sharply at the boundry and increase exponentially again in the thin layer of magnetic material 12, rising to a maximum at the outside 25 of the magnetic material and then falling to zero. The skin depth thick ness '6 may be defined by the equation:

where f is the frequency of operation, u the maximum permeability of the conductor, and is the conductiv ity. in a preferred embodiment, the skin depth thickness for the magnetic material and the copper conductor were estimated to be 0.62 microns and 4.6 microns thick respectively at 350 megahertz. The actual thickness of the magnetic layer was approximately 10,000A or 1.0 micron. 1n the preferred embodiment explained hereinbefore the thin layer of magnetic material was thicker than the skin depth thickness. As frequencies increase the skin depth thickness will decrease, and if the thin layer of magnetic material is not reduced accordingly, attenuation of the electric field will result.

The thin layer of magnetic material 12 is preferably conductive and conductively attached to the center conductor 11 so that the radial electric field is continuous. When the electric field is continuous at the boundry, the conduction current is divided inversely proportional to the skin depth thicknesses of the two materials. it can be shown that highly conductive Permalloy having a small skin depth thickness will conduct a much larger amount of conduction current at high frequencies than the percentage increase in diameter of the center conductor. Since this phenomenon is true for one conductive layer of material having a different resistance, it is true for multiple layers of material having different resistances which are conductively connected or arranged in a continuous electric field to independantly support conductive skin layers.

Not only does the thin layer of magnetic material conduct a portion of conventional current, but it enhances conduction of some form of wave energy. Without changing the conductivity of the magnetic material in a piece of novel cable, it was annealed partially destroying the circumferential orientation of the easy axis. As a result of the annealing the characteristic impedance 2,; 1} L lC increased which is attributed to an increase in aforementioned permeability s s and p. however, the time delay increased more than can be accounted for by any possible increase in permeability. The propagation of the wave energy is enhanced by the aforementioned circumferential orientation of the uniaxial anisotropic magnetic material. It may be possible that the partial annealing caused the shape of the B vs H curve to change, thus the operation on a vertical slope region of the B vs H curve causes hysteresis losses, flux changes and time delays which did not occur when operating on a saturation portion of the curve of square loop material described in FIG. 4.

Another explanation for the dc crease in time delay T is made with reference to F IL]. 6 showing a schematic network representation of the new coaxial cable. The shunt arm 26 of the equivalent Tee network was found to have an inductive reactance 27 in series with the shunt capacitance 28 which lowers the resonance point or cutoff point compared to coaxial cables without the thin layer of magnetic material. At high frequencies above the cut off point, usually above 20 megahertz where fast rise time of sub nanosecond pulse power is operable, the inductive reactance 27 (X is very large and tends to cancel out the capacitive reactance 28 (X Above the cut off frequency the shunt arm 26 appears highly inductive so that the center conductor 11 is substantially isolated from the shield-return 13. When isolation occurs the time delay T is no longer equal to 4 LC and the speed of propagation begins to approach the speed of light as is achieved in an open conductor, however, the skin effect losses and radiation losses which accompany open conductors have been reduced to those associated with standard coaxial cables.

Part of the current conducted in the layer of magnetic material may be forced into a helical path which helps to explain the increase in inductive reactance and the high magnetic field.

Another desirable feature of employing Permalloy Ni Fe materials is to achieve reduced phase distortion. At high frequencies Permalloy acts as a magnetic damper providing a desirable roll off characteristic. This characteristic substantially attenuates the frequencies above the operating frequencies which would otherwise provide phase distortion.

While this invention has been described with respect to particular embodiments employing a particular high anisotropy substantially circumferentially oriented magnetic material it is apparent that other magnetic materials can be found which have the desirable characteristic described hereinbefore. The coaxial transmission cable and method for reducing time delay and attenuation have been described as best available theoretical analysis will now permit. Other embodiments for reducing the size of coaxial cables for high frequency use without increasing time delay and attenuation will become apparent to those skilled in this art.

we claim:

1. in a communication system having means for generating high frequency electro magnetic energy pulses I representing intelligence, a coaxial cable for transmitting said pulses, and means for receiving said pulses, said cable comprising in combination:

an electrical center conductor, a magnetizable material at the outside surface of said center conductor, said magnetizable material being magnetically oriented to provide a magnetic field which is substantially circumferentially around said center conductor.

electrically insulating dielectric material disposed to cover said center conductor,

an electrical outer conductor formed to provide a shield around said dielectric material,

said center conductor, said outer conductor, and said dielectric material disposed together to form said coaxial cable,

said magnetizable magnetic material being magnetically oriented in a direction to provide a sufficient magnetic field within said coaxial cable to enhance electro magnetic energy pulse propagation velocy.

whereby high frequency electro magnetic pulses from the generating means will travel through said coaxial cable means to said receiving means faster than would occur without said magnetic field. 2. A coaxial cable as set forth in claim 1 wherein said magnetizable magnetic material is magnetically oriented to provide an easy axis of magnetization in a direction which is substantially circumferential around the outside of said center conductor.

3. An improved flexible miniaturized coaxial cable of the type employed in transmitting very high frequency pulses having magnetic loading comprising:

a flexible center conductor having an outside diameter d,

said flexible center conductor comprising a conductive magnetic material at the outside diameter d having a high permeability creating an increased resultant permeability u, in the cable.

said conductive magnetic material having a crystalline grain structure and having an easy axis of magnetization at least partially oriented to provide an internal magnetic field in a circumferential direction,

flexible dielectric material spacer means surrounding said center conductor having an outside diameter D and a dielectric constant e, and a flexible conductive shield supported on and surrounding the outside of said dielectric spacer means and having an inside diameter D whereby the characteristic impedance of said improved flexible cable Z 1/211' s n /e log D /d is increased by an increase in M through magnetic loading and the time delay T is increased by an amount less than I p /e by providing said internal magnetic field.

4. An improved flexible coaxial transmission cable of the type set forth in claim 3 wherein said conductive magnetic material comprises nickel and iron.

5. An improved flexible coaxial transmission cable of the type set forth in claim 4 wherein said conductive magnetic material comprises Permalloy having very low magnetostrictive characteristics.

6. An improved flexible coaxial transmission cable of the type set forth in claim 3 wherein said center con ductor comprises a thin layer of magnetic material greater than 500A and less than 15,000A thick and is thin enough to maintain uniaxial anisotropy in a circumferential direction.

7. An improved flexible coaxial transmission cable of the type set forth in claim 3 wherein said conductive magnetic material comprises a thin layer having a thickness which is greater than the skin depth thickness at the frequency of operation.

8. An improved flexible miniaturized coaxial cable as set forth in claim 3 further characterized in that said center conductor comprises a very good conductive magnetic material center and an outside layer of conductive magnetic material having a preferred magnetic field oriented in a circumferential direction.

9. An improved flexible coaxial transmission cable for use in the transmission of very high frequency pulses of the type having magnetic loading for decreasing attenuation by increasing the inductance L and the characteristic impedance Z comprising:

a flexible inner center conductor of low resistance material having an outside diameter d.

a flexible outer shield of low resistance material surrounding said center conductor and having an inside diameter D,

a flexible dielectric spacer disposed between said center conductor and said shield, said elements forming a flexible coaxial cable having a characteristic impedance Z, V L lC and a time delay T L C, where C is the shunt capacitance,

a layer of flexible circumferentially oriented high permeability magnetic material formed on the outside of said center conductor, said elements now forming a coaxial cable having a resultant characteristic impedance Z,= L /C where the resultant inductance L, L and the resultant time delay T of very high frequency pulses is substan tially less than V L C.

10. An improved flexible coaxial transmission cable as set forth in claim 9 wherein said layer of high permeability magnetic material is electrically conductive nickel-iron having a thickness between 500A to 15,000A and is uniaxial anisotropic.

11. An improved flexible coaxial transmission cable as set forth in claim 10 wherein said layer of circumferential oriented magnetic material and said center conductor form concentric conduction paths for high frequency pulse current concentrated in a skin effect pat' tern at high frequencies.

12. An improved flexible coaxial transmission cable as set forth in claim 11 wherein the current flow in said conduction paths is substantially proportional to the conductivity of the conduction path.

13. An improved flexible coaxial transmission cable for use in the transmission of very high frequency pulses comprising:

a flexible inner center conductor of low resistance material having an outside diameter d,

a flexible outer shield of low resistance material surrounding said center conductor and having an in side diameter D.

a flexible dielectric spacer between said conductor and said shield, and

a layer of magnetic material formed at the outside of said center conductor and having a high permeability and an easy axis of magnetization oriented in a circumferential direction.

said center conductor and said layer of magnetic material formed to provide a conduction path for conventional current,

said layer of magnetic material providing a path for the conduction of very high frequency pulse energy, whereby said coaxial cable is rendered capable of transmitting more energy at higher wave propagation rates than conventional coaxial cables.

cent without a change in the characteristic impedance Z by the addition of said layer of magnetic material.

16. An improved flexible coaxial transmission cable as set forth in claim 15 wherein the 0/0 ratio is reduced by decreasing the inside diameter D of said outer shield and the thickness of said wave-sustaining dielectric spacen 

1. In a communication system having means for generating high frequency electro magnetic energy pulses representing intelligence, a coaxial cable for transmitting said pulses, and means for receiving said pulses, said cable comprising in combination: an electrical center conductor, a magnetizable material at the outside surface of said center conductor, said magnetizable material being magnetically oriented to provide a magnetic field which is substantially circumferentially around said center conductor. electrically insulating dielectric material disposed to cover said center conductor, an electrical outer conductor formed to provide a shield around said dielectric material, said center conductor, said outer conductor, and said dielectric material disposed together to form said coaxial cable, said magnetizable magnetic material being magnetically oriented in a direction to provide a sufficient magnetic field within said coaxial cable to enhance electro magnetic energy pulse propagation velocity, whereby high frequency electro magnetic pulses from the generating means will travel through said coaxial cable means to said receiving means faster than would occur without said magnetic field.
 2. A coaxial cable as set forth in claim 1 wherein said magnetizable magnetic material is magnetically oriented to provide an easy axis of magnetization in a direction which is substantially circumferential around the outside of said center conductor.
 3. An improved flexible miniaturized coaxial cable of the type employed in transmitting very high frequency pulses having magnetic loading comprising: a flexible center conductor having an outside diameter d, said flexible center conductor comprising a conductive magnetic material at the outside diameter d having a high permeability creating an increased resultant permeability Mu r in the cable, said conductive magnetic material having a crystalline grain structure and having an easy axis of magnetization at least partially oriented to provide an internal magnetic field in a circumferential direction, flexible dielectric material spacer means surrounding said center conductor having an outside diameter Dr and a dielectric constant epsilon , and a flexible conductive shield supported on and surrounding the outside of said dielectric spacer means and having an inside diameter D whereby the characteristic impedaNce of said improved flexible cable Z 1/2 pi Square Root Mu R/ epsilon log Dr/d is increased by an increase in Mu r through magnetic loading and the time delay Tr is increased by an amount less than Square Root Mu R/ epsilon by providing said internal magnetic field.
 4. An improved flexible coaxial transmission cable of the type set forth in claim 3 wherein said conductive magnetic material comprises nickel and iron.
 5. An improved flexible coaxial transmission cable of the type set forth in claim 4 wherein said conductive magnetic material comprises Permalloy having very low magnetostrictive characteristics.
 6. An improved flexible coaxial transmission cable of the type set forth in claim 3 wherein said center conductor comprises a thin layer of magnetic material greater than 500A and less than 15,000A thick and is thin enough to maintain uniaxial anisotropy in a circumferential direction.
 7. An improved flexible coaxial transmission cable of the type set forth in claim 3 wherein said conductive magnetic material comprises a thin layer having a thickness which is greater than the skin depth thickness at the frequency of operation.
 8. An improved flexible miniaturized coaxial cable as set forth in claim 3 further characterized in that said center conductor comprises a very good conductive magnetic material center and an outside layer of conductive magnetic material having a preferred magnetic field oriented in a circumferential direction.
 9. An improved flexible coaxial transmission cable for use in the transmission of very high frequency pulses of the type having magnetic loading for decreasing attenuation by increasing the inductance Lo and the characteristic impedance Zo, comprising: a flexible inner center conductor of low resistance material having an outside diameter d, a flexible outer shield of low resistance material surrounding said center conductor and having an inside diameter D, a flexible dielectric spacer disposed between said center conductor and said shield, said elements forming a flexible coaxial cable having a characteristic impedance Zo Square Root Lo/C and a time delay To Square Root LoC, where C is the shunt capacitance, a layer of flexible circumferentially oriented high permeability magnetic material formed on the outside of said center conductor, said elements now forming a coaxial cable having a resultant characteristic impedance Zr Square Root LR/C where the resultant inductance Lr > Lo, and the resultant time delay Tr of very high frequency pulses is substantially less than Square Root LrC.
 10. An improved flexible coaxial transmission cable as set forth in claim 9 wherein said layer of high permeability magnetic material is electrically conductive nickel-iron having a thickness between 500A to 15,000A and is uniaxial anisotropic.
 11. An improved flexible coaxial transmission cable as set forth in claim 10 wherein said layer of circumferential oriented magnetic material and said center conductor form concentric conduction paths for high frequency pulse current concentrated in a skin effect pattern at high frequencies.
 12. An improved flexible coaxial transmission cable as set forth in claim 11 wherein the current flow in said conduction paths is substantially proportional to the conductivity of the conduction path.
 13. An improved flexible coaxial transmission cable for use in the transmission of very high frequency pulses comprising: a flexible inner center conductor of low resistance material having an outside diameter d, a flexible outer shield of low resistance material surrounding said center conductor and having an inside diameter D, a flexible dielectric spacer between said conductor and said shield, and a layer of magnetic material formed at the outside of said center conductor and having a high permeability and an easy axis of magnetization oriented in a circumferential direction, said center conductor and said layer of magnetic material formed to provide a conduction path for conventional current, said layer of magnetic material providing a path for the conduction of very high frequency pulse energy, whereby said coaxial cable is rendered capable of transmitting more energy at higher wave propagation rates than conventional coaxial cables.
 14. An improved flexible coaxial transmission cable as set forth in claim 13 wherein said layer of magnetic material is a low magnetostrictive Permalloy plated over a plated conductive base on said center conductor.
 15. An improved flexible coaxial transmission cable as set forth in claim 13 wherein the usual D/d ratio for unloaded coaxial cable is reduced by at least thirty percent without a change in the characteristic impedance Z by the addition of said layer of magnetic material.
 16. An improved flexible coaxial transmission cable as set forth in claim 15 wherein the D/d ratio is reduced by decreasing the inside diameter Dr of said outer shield and the thickness of said wave-sustaining dielectric spacer. 